Klingersil® C-4401
General Application Gasketing
|
Distinguishing Characteristics & Applications |
|
|
Synthetic Fiber |
Resistance |
|
|
Nitrile Binder |
Good Creep |
|
|
Excellent Sealability |
Relaxation |
|
|
Excellent Chemical |
General Purpose Sheet |
|
|
|
|
|
|
Typical values refer to 1/16" material unless otherwise
specified. |
|
Creep Relaxation |
ASTM F38B (1/32") |
20% |
|
Sealability |
ASTM F37A (1/32") |
<0.25 ml/hr |
|
Gas Permeability |
DIN 3535/6 |
<0.5 ml/min |
|
Compressibility |
ASTM F36J |
7% |
|
Recovery |
ASTM F36J |
50% minimum |
|
|
|
|
|
Klinger Hot Compression Test |
|
|
Thickness Decrease 73°F (23°C) |
10.5% initial |
|
Thickness Decrease 572°F (300°C) |
17% additional |
|
|
|
|
|
Weight Increase |
|
|
|
ASTM F146 after immersion in Fuel B |
10% maximum |
|
5h/73°F (23°C) |
|
|
|
|
|
|
|
Thickness Increase |
|
|
|
ASTM F146 after immersion in |
|
|
|
ASTM Oil 1, 5h/300°F (149°C) |
|
0-5% |
|
ASTM Oil IRM903, 5h/300°F (149°C) |
0-5% |
|
ASTM Fuel A, 5h/73°F (23°C) |
|
0-5% |
|
ASTM Fuel B, 5h/73°F (23°C) |
|
0-7% |
|
|
|
|
|
Dielectric Strength |
|
|
|
ASTM D149-95a |
|
14 kV/mm |
|
|
|
|
|
ASTM F104 Line Call Out |
|
F712121B3E12K6M5 |
|
|
|
|
|
Leachable Chloride Content |
|
|
|
FSA Method (Typical) |
|
100 ppm |
|
|
|
|
|
Density |
|
112 lb/ft3
(1.8 g/cc) |
|
|
|
|
|
Color (Top/Bottom) |
|
Green |
|
Pressure & Temperature Graphs |
Liquids
 |
Gases & Steam
 |
Klingersil® C-4409
Metal Re-enforced Gasketing
|
Distinguishing Characteristics & Applications |
|
|
Synthetic Fiber |
Excellent in Hot Gases |
|
|
Nitrile Binder |
Replaces Spiral Wounds |
|
|
High Temperature & Stress |
Vibration |
|
|
Galvanized Low Carbon Steel Insert |
|
|
|
|
|
|
Typical values refer to 1/16" material unless otherwise
specified. |
|
Creep Relaxation |
ASTM F38B (1/32") |
20% |
|
Compressibility |
ASTM F36J |
7% |
|
Recovery |
ASTM F36J |
50% minimum |
|
|
|
|
|
Klinger Hot Compression Test |
|
|
Thickness Decrease 73°F (23°C) |
10% initial |
|
Thickness Decrease 572°F (300°C) |
10% additional |
|
|
|
|
|
Weight Increase |
|
|
|
ASTM F146 after immersion in Fuel B |
10% maximum |
|
5h/73°F (23°C) |
|
|
|
|
|
|
|
Thickness Increase |
|
|
|
ASTM F146 after immersion in |
|
|
|
ASTM Oil 1, 5h/300°F (149°C) |
|
0-5% |
|
ASTM Oil IRM903, 5h/300°F (149°C) |
0-3% |
|
ASTM Fuel A, 5h/73°F (23°C) |
|
0-5% |
|
ASTM Fuel B, 5h/73°F (23°C) |
|
0-5% |
|
|
|
|
|
ASTM F104 Line Call Out |
|
F712112B3E11M8 |
|
|
|
|
|
Density |
|
125 lb/ft3
(2.0 g/cc) |
|
|
|
|
|
Color (Top/Bottom) |
|
Green |
|
Pressure & Temperature Graphs |
Liquids
 |
Gases & Steam
 |
Klingersil® C-4433
Compressed Inorganic Fiber
Gasketing
|
Distinguishing Characteristics & Applications |
|
|
Nitrile Binder |
Excellent Creep Relaxation |
|
|
Ultimate Steam Sheet |
Best General Purpose Sheet |
|
Outstanding Load Bearing |
|
|
|
|
|
|
|
Typical values refer to 1/16" material unless otherwise
specified. |
|
Creep Relaxation |
ASTM F38B (1/32") |
20% |
|
Sealability |
ASTM F37A (1/32") |
<0.5 ml/hr |
|
Gas Permeability |
DIN 3535/6 |
<0.2 ml/min |
|
Compressibility |
ASTM F36J |
7% |
|
Recovery |
ASTM F36J |
60% minimum |
|
|
|
|
|
Klinger Hot Compression Test |
|
|
Thickness Decrease 73°F (23°C) |
7% initial |
|
Thickness Decrease 572°F (300°C) |
8% additional |
|
|
|
|
|
Weight Increase |
|
|
|
ASTM F146 after immersion in Fuel B |
10% maximum |
|
5h/73°F (23°C) |
|
|
|
|
|
|
|
Thickness Increase |
|
|
|
ASTM F146 after immersion in |
|
|
|
ASTM Oil 1, 5h/300°F (149°C) |
|
0-5% |
|
ASTM Oil IRM903, 5h/300°F (149°C) |
0-4% |
|
ASTM Fuel A, 5h/73°F (23°C) |
|
0-5% |
|
ASTM Fuel B, 5h/73°F (23°C) |
|
0-7% |
|
|
|
|
|
Dielectric Strength |
|
|
|
ASTM D149-95a |
|
21 kV/mm |
|
|
|
|
|
ASTM F104 Line Call Out |
|
F712132B3E12K6M5 |
|
|
|
|
|
Leachable Chloride Content |
|
|
|
FSA Method (Typical) |
|
150 ppm |
|
|
|
|
|
Density |
|
112 lb/ft3
(1.8 g/cc) |
|
|
|
|
|
Color (Top/Bottom) |
|
Red |
|
Pressure & Temperature Graphs |
Liquids
 |
Gases & Steam
 |
Klingersil® C-4500
Carbon Fiber Gasketing
|
Distinguishing Characteristics & Applications |
|
|
Carbon Fiber |
Good Steam Sheet |
|
|
Nitrile Binder |
Suitable for a wide range |
|
|
High Temperature |
of chemical applications |
|
|
High Internal Pressure |
|
|
|
|
|
|
|
Typical values refer to 1/16" material unless otherwise
specified. |
|
Creep Relaxation |
ASTM F38B (1/32") |
20% |
|
Sealability |
ASTM F37A (1/32") |
<0.30 ml/hr |
|
Gas Permeability |
DIN 3535/6 |
<1.0 ml/min |
|
Compressibility |
ASTM F36J |
12% |
|
Recovery |
ASTM F36J |
60% minimum |
|
|
|
|
|
Klinger Hot Compression Test |
|
|
Thickness Decrease 73°F (23°C) |
10% initial |
|
Thickness Decrease 572°F (300°C) |
15% additional |
|
|
|
|
|
Weight Increase |
|
|
|
ASTM F146 after immersion in Fuel B |
10% maximum |
|
5h/73°F (23°C) |
|
|
|
|
|
|
|
Thickness Increase |
|
|
|
ASTM F146 after immersion in |
|
|
|
ASTM Oil 1, 5h/300°F (149°C) |
|
0-5% |
|
ASTM Oil IRM903, 5h/300°F (149°C) |
0-3% |
|
ASTM Fuel A, 5h/73°F (23°C) |
|
0-5% |
|
ASTM Fuel B, 5h/73°F (23°C) |
|
0-5% |
|
|
|
|
|
Dielectric Strength |
|
|
|
ASTM D149-95a |
|
1.5 kV/mm |
|
|
|
|
|
ASTM F104 Line Call Out |
|
F712122B3E11K6M5 |
|
|
|
|
|
Leachable Chloride Content |
|
|
|
FSA Method (Typical) |
|
200 ppm |
|
|
|
|
|
Density |
|
87 lb/ft3
(1.4 g/cc) |
|
|
|
|
|
Color (Top/Bottom) |
|
Black |
|
Pressure & Temperature Graphs |
Liquids
 |
Gases & Steam
 |
Klingersil® C-7400
Chemical Resistant Gasketing
|
Distinguishing Characteristics & Applications |
|
|
Synthetic Fiber |
Good Oil Swell Characteristics |
|
EPDM Binder |
Excellent Aging Properties |
|
|
Moderate Caustics and Acids |
Good in Light Duty Steam |
|
|
|
|
|
|
Typical values refer to 1/16" material unless otherwise
specified. |
|
Creep Relaxation |
ASTM F38B (1/32") |
25% |
|
Sealability |
ASTM F37A (1/32") |
<0.30 ml/hr |
|
Gas Permeability |
DIN 3535/6 |
<0.5 ml/min |
|
Compressibility |
ASTM F36J |
7% |
|
Recovery |
ASTM F36J |
50% minimum |
|
|
|
|
|
Klinger Hot Compression Test |
|
|
(tested at 3,625-psi gasket stress) |
|
|
Thickness Decrease 73°F (23°C) |
9% initial |
|
Thickness Decrease 572°F (300°C) |
5% additional |
|
|
|
|
|
Weight Increase |
|
|
|
ASTM F146 after immersion in Fuel B |
15% maximum |
|
5h/73°F (23°C) |
|
|
|
|
|
|
|
Thickness Increase |
|
|
ASTM F146 after immersion in ASTM Oil 1
5h/300°F (149°C) |
0-15% |
|
ASTM Oil IRM903, 5h/300°F (149°C) |
15-30% |
|
ASTM Fuel A, 5h/73°F (23°C) |
|
0-20% |
|
ASTM Fuel B, 5h/73°F (23°C) |
|
5-20% |
|
|
|
|
|
Dielectric Strength |
|
|
|
ASTM D149-95a |
|
22 kV/mm |
|
|
|
|
|
ASTM F104 Line Call Out |
|
F712441B4E24K6M5 |
|
|
|
|
|
Leachable Chloride Content |
|
|
|
FSA Method (Typical) |
|
200 ppm |
|
|
|
|
|
Density |
|
94 lb/ft3
(1.5 g/cc) |
|
|
|
|
|
Color (Top/Bottom) |
|
White/Grey |
|
Pressure & Temperature Graphs |
Liquids
 |
Gases & Steam
 |
|